It is a self-leveling, two component, hard-elastic, self-leveling polyurethane coating with high impact and abrasion strength and very good resistance to acidic and basic solutions, used for self-leveling floor coating constructions. Cures by reaction (cross linking) of the two components. The Product give surface Resistance to several organic chemicals used in the food industry makes the system suitable for use in various food processing industries.
Usage areas:
As an easy to apply self-leveling floor coating with excellent adherence and resistant to cigarette burns, it is easy to clean to create a hygienic environment, the product has is crack bridging properties (1.6 – 2.9 mm), elastic, sound absorbent (4 db depending on the application thickness) and have an attractive finish. The product can be used in hospitals & nursing homes & pharmaceutical industries, libraries, schools, meeting rooms & offices, hotels, exhibition halls, Physician practices, Shopping centers, cold Storage rooms, meat, poultry and fish processing plants, bakeries & confectionery industries ……..etc.
Application Details:
New Concrete: Remove laitance by power grinding, vacuum grit blasting or hydrochloric acid etching. Choose the method best suited for the premises. After grinding remove dust carefully with a vacuum cleaner. Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water). Rinse with plenty of water. Dry the floor.
Application prohibitions:
Use only where application and drying can proceed at temperatures above: 10°C/50°F. The temperature of paint itself should be 15°C/59°F or above. Apply only on a dry and clean surface with a Temperature above the dew point to avoid condensation. In confined spaces provide adequate ventilation during application and drying.
Coated surfaces should be protected from moisture for 4-6 hours after application. Moisture may whiten the surface or/and make it sticky. It may also disturb hardening. Faded or sticky layers in parts of the surface should be removed by grinding or milling and laid again.