The 100% pure polyurea was developed as a two-component, spray able, aromatic coating suitable for waterproofing, protection and sealing in general. It’s made up of two high reactive liquid components, isocyanates and amines, which are mixed together using specific spray equipment, to form an aromatic, continuous, seamless, high density, solid and elastic pure polyurea membrane, with high mechanical and chemical resistance qualities.
Usage areas:
For waterproofing and protection of:
ROOFING: Sloped and flat roofs (walk-able), balconies and overhangs.
FLOORING: Car parks with heavy traffic, industrial floor surfaces with waterproofing and hard-wearing requirements including an approved non-slip finish.
BRIDGE DECK: coating under asphalt on concrete elements of civil engineering.
Tanks and irrigation canals, potable water contact. Retaining walls and foundations. Green roofs and walls. Power plants, recycling, water waste, water treatment and petrochemical plants. Swimming pools, aquariums, lakes. Near sea water Vehicle and boat coatings (bed liners) Asbestos roofs rehabilitation.
Application Details:
Surface preparation strongly affects the coating performance. Concrete substrates must be prepared mechanically using abrasive blast cleaning to remove cement laitance and achieve an open textured surface. Weak concrete must be removed and surface defects such as voids must be fully exposed. Repairs to the substrate, filling of blowholes/voids and surface leveling must be carried out using Epoxy Fıller. All dust, loose and friable material must be completely removed from all surfaces before application of the product, preferably by brush and/or vacuum. For application pull off strength of the surface should be min. 1.5 N/mm² and concrete residual moisture should be max. 4% pbw (with an appropriate moisture tolerant primer should be max. 6% pbw). The moisture content should be measured by moisture meter. Be aware of condensation; the substrate must be at least 3 °C above dew point to reduce the risk of condensation of the coating. Relative air humidity for application should be lower than 85%. Prior to application, confirm substrate moisture content, relative air humidity and dew point.
Application prohibitions:
Component A of the product contains isocyanine. Do not smoke during application process and work in a well-ventilated environment away from bare flame. Do not forget that solvents are heavier than air and therefore they accumulate on floor. Wear suitable protective clothing, gloves and eye/ face protection. Adequate ventilation of the working area is recommended.